The effect of maleic anhydride (MA) content on morphological, thermal, thermomechanical and mechanical properties of PA6/AES/MMA-MA (66.5/28.5/5 wt%) system was investigated. In general, the simple incorporation of MMA-MA to PA6/AES system is responsible for enhancements in mechanical performance. PA6/AES/MMA-MA3% and PA6/AES/MMA5% exhibited similar morphology and final properties, indicating no MA content effect on the studied system. On the other hand, PA6/AES/MMA-MA10% exhibited a quite different morphology and lower mechanical performance compared to the other compatibilized blends. Such unexpected behavior was not attributed to the effective maleic anhydride content in this composition, but to the reduced molar mass resulted from the excess of non-reacted MA monomer during the synthesis procedure.

O efeito da organofilização da argila no comportamento mecânico, morfológico e termo-mecânico de nanocompósitos baseados em blendas de poliamida 6 )/acrilonitrila-EPDM-estireno foi estudado. Três nanoargilas foram utilizadas para a preparação dos nanocompósitos: duas montmorilonitas comerciais modificadas organicamente (Cloisite®30B and Cloisite® 20A) e uma montmorilonita sódica não modificada (Cloisite®Na+). Difração de raios-X em alto ângulo, microscopia eletrônica de transmissão e testes de tração e resistência ao impacto foram utilizados para avaliar o efeito da organofilização da nanoargila na morfologia e propriedades mecânicas dos materiais. As propriedades termo-mecânicas foram avaliadas por análise dinâmico mecânica e temperatura de deflexão térmica. Os resultados mostraram que a modificação da nanocarga afeta simultaneamente o grau de reforço da matriz, dispersão das lamelas de argila na blenda e tamanho da fase dispersa AES. A adição das diferentes nanoargilas aumenta o módulo elástico de todos os nanocompósitos ternários em relação à blenda pura sem argila. Por outro lado, um aumento na tenacidade foi obtido apenas para os sistemas com Cloisite®Na+. Um aumento significativo no módulo de armazenamento e HDT foi observado pela incorporação da Cloisite®30B na blenda.

The effect of clay organophilization on mechanical, morphological and thermo-mechanical behavior of polyamide-6/acrylonitrile-EPDM (ethylene/propylene/diene elastomer)-styrene blends was studied. Three nanoclays were used for the preparation of nanocomposites: two commercial organically modified montmorillonites (Cloisite®30B and Cloisite® 20A) and an unmodified sodium montmorillonite (Cloisite®Na+). We used wide angle X-ray scattering, transmission electron microscopy and mechanical tests to evaluate the effect of clay modification on the morphology and mechanical properties of the nanocomposites. The thermo-mechanical properties were characterized using dynamic mechanical analysis and heat distortion temperature (HDT). The results show that the modification of clay affected simultaneously the degree of PA6 matrix reinforcement, dispersion of the clay lamellas in the blend and size of the dispersed phase AES. The incorporation of different nanoclays increase the elastic modulus of all the ternary nanocomposites compared to the neat blend. An increase in the toughness is obtained only for systems with Cloisite®Na+. A significant increment in the storages modulus and HDT was observed by the incorporation of Cloisite®30B in the PA6/AES blends.